products

Resin SZUV-C6006-transparent

Short Tlhaloso:

SZUV-C6006 is a transparent resin for SLA 3D printer.

3D Khatiso Materials


Product Qaqileng

Video

Printing Instructions

Product Tags

3D Khatiso Materials

Transparent Resin-SZUV-C6006

Selelekela sa 3D Khatiso Materials

litšobotsi tse

SZUV-C6006

TLHALOSO EA SEHLAHISOA 

SZUV-C6006 is a clear SL resin which has accurate and durable features. It is designed for solid state SLA printers.

SZUV-C6006 can be applied in master patterns, concept models, general parts and functional prototypes in the field of automotive, medical and consumer electronics industries.

tloaelehileng LIHLOOHO TSE HLAHANG

-Medium viscosity, so easy for recoating, easy to clean parts and machines 

-Improved strength retention, improved dimensions retention of parts in humid condition 

-Good strength, need minimal part finishing 

tloaelehileng MELEMO

-Superior clear, building parts with outstanding clarity and excellent accuracy 

-Need less part finishing time, easier post-curing 

Physical Properties (Liquid) 

Ponahalo e hlakile
segokanyipalo 1.12g / cm, 3 @ 25 ℃
e tiileng e qamathelang 408cps @ 26 ℃
DP 0,18 limilimithara
EC 6,7 MJ / cm, 2
Building lera le tsona ka botenya 0.1mm

 Mechanical Properties (Post-Cured)

lekanya Teko mokhoa BOHLOKOA
    90 metsotso UV poso-pheko
Thatafala, Shore D ASTM D 2240 83
Flexural modulus, Mpa ASTM D 790 2,680-2,790
Flexural matla, Mpa ASTM D 790 75- 83
Tensile modulus, MPa ASTM D 638 2,580-2,670
Tensile matla, MPa ASTM D 638 45-60
Elongation ka khefu ASTM D 638 11-20%
Tshusumetso matla, notched lzod, J / limithara  ASTM D 256  38 - 48 
Mocheso deflection mocheso, ℃  ASTM D ho 648 @ 66PSI  52 
Glass transition, Tg 

DMA, E' peak

62

 

 


  • Previous:
  • Next:

  •  

    Fumaneha ka le 'ngoe scan ninemanga.com lebelo, limilimithara / s Suggested single scanning speed, mm/s
    mocheso lehoakhoa 18-25℃ 23℃ without heating
    mongobo tikoloho ya 38% tlase 36%below
    matla a ka laser 300mw 300mw
    support scanning speed ≤1500 1200
    scanning interval ≤0.1mm 0.08mm
    Ea moeli anthivaerase lebelo
    ≤7000 2000
    Tlatsa anthivaerase lebelo ≥4000 7500

     

     