Print Material-Transparent resin-6006
Introduction of 3D Printing Materials
Characteristics
SZUV-C6006
PRODUCT DESCRIPTION
SZUV-C6006 is a clear SL resin which has accurate and durable features. It is designed for solid state SLA platforms. SZUV-C6006 can be applied in master patterns, concept models, general parts and functional prototypes in the field of automotive, medical and consumer electronics industries. SZUV-C6006
TYPICAL FEATURES
-Liquid resin`s medium viscosity, so easy recoating, easy clean parts and machines
-Improved strength retentin, improved dimensions retention of parts in humid condition
-Good green strength, so need minimal part finishing
TYPICAL BENEFITS
-Superior clear,building patrs with outstanding clarity and excellent accuracy
-Need less part finishing time,easier post-curing
Physical Properties – Liquid Material
| Appearance | Clear |
| Density | 1.12g/cm3 @ 25 ℃ |
| Viscosity | 408cps @ 26 ℃ |
| Dp | 0.18 mm |
| Ec | 6.7 mJ/cm2 |
| Building layer thickness | 0.1mm |
Mechanical Properties of Post-Cured Material
| MEASUREMENT | TEST METHOD | VALUE |
| 90-minute UV post-cure | ||
| Hardness, Shore D | ASTM D 2240 | 83 |
| Flexural modulus, Mpa | ASTM D 790 | 2,680-2,790 |
| Flexural strength, Mpa | ASTM D 790 | 75- 83 |
| Tensile modulus, MPa | ASTM D 638 | 2,580-2,670 |
| Tensile strength, MPa | ASTM D 638 | 45-60 |
| Elongation at break | ASTM D 638 | 11-20% |
| Impact strength,notched lzod, J/m | ASTM D 256 | 38 - 48 |
| Heat deflection temperature, ℃ | ASTM D 648 @66PSI | 52 |
| Glass transition,Tg |
DMA，E”peak |
62 |
|
|
Available in single scan speed, mm/s |
Suggested that single scanning speed, mm/s |
|
|
resin temperature |
18-25℃ |
23℃ |
Without heating |
|
environment humidity |
38%below |
36% below |
|
|
laser power |
300mw |
300mw |
|
|
Scanning interval |
≤0.1mm |
0.08mm |
|
|
Support scanning speed |
≤1500 |
1200 |
|
|
Contour scanning speed |
≤7000 |
2000 |
|
|
Fill scanning speed |
≥4000 |
7500 |
|