Resin SZUV-C6006-transparent
La introducció de materials d'impressió 3D
característiques
SZUV-C6006
DESCRIPCIÓ DEL PRODUCTE
SZUV-C6006 is a clear SL resin which has accurate and durable features. It is designed for solid state SLA printers.
SZUV-C6006 can be applied in master patterns, concept models, general parts and functional prototypes in the field of automotive, medical and consumer electronics industries.
TÍPICS CARACTERÍSTIQUES
-Medium viscosity, so easy for recoating, easy to clean parts and machines
-Improved strength retention, improved dimensions retention of parts in humid condition
-Good strength, need minimal part finishing
TÍPICS BENEFICIS
-Superior clear, building parts with outstanding clarity and excellent accuracy
-Need less part finishing time, easier post-curing
Physical Properties (Liquid)
aparença | clar |
densitat | 1,12 g / cm 3 @ 25 ℃ |
Viscositat | 408cps @ 26 ℃ |
dp | 0,18 mm |
CE | 6,7 mJ / cm 2 |
gruix de la capa de construcció | 0,1 mm |
Mechanical Properties (Post-Cured)
MESURA | MÈTODE DE PROVA | VALOR |
UV de 90 minuts post-curat | ||
Duresa, Shore D | ASTM D 2240 | 83 |
Mòdul de flexió, Mpa | ASTM D 790 | 2,680-2,790 |
resistència a la flexió, Mpa | ASTM D 790 | 75- 83 |
El mòdul de tracció, MPa | ASTM D 638 | 2,580-2,670 |
Resistència a la tracció, MPa | ASTM D 638 | 45-60 |
Allargament al trencament | ASTM D 638 | 11-20% |
La resistència a l'impacte, lzod osques, J / m | ASTM D 256 | 38-48 |
Heat temperatura de deflexió, ℃ | ASTM D 648 @ 66PSI | 52 |
Glass transition, Tg |
DMA, E' peak |
62 |
Disponible en una sola exploració velocitat, mm / s | Suggested single scanning speed, mm/s | ||
temperatura de la resina | 18-25℃ | 23℃ | without heating |
humitat de l'ambient | El 38% per sota | 36%below | |
potència del làser | 300MW | 300MW | |
support scanning speed | ≤1500 | 1200 | |
scanning interval | ≤0.1mm | 0.08mm | |
velocitat d'escaneig de contorn |
≤7000 | 2000 | |
Omplir la velocitat d'escaneig | ≥4000 | 7500 |