SZUV-C6006

ngwaahịa nkọwa 

SZUV-C6006 is a clear SL resin which has accurate and durable features. It is designed for solid state SLA printers.

SZUV-C6006 can be applied in master patterns, concept models, general parts and functional prototypes in the field of automotive, medical and consumer electronics industries.

ahụkarị atụmatụ

-Medium viscosity, so easy for recoating, easy to clean parts and machines 

-Improved strength retention, improved dimensions retention of parts in humid condition 

-Good strength, need minimal part finishing 

ahụkarị URU Ọ BARA

-Superior clear, building parts with outstanding clarity and excellent accuracy 

-Need less part finishing time, easier post-curing 

Physical Properties (Liquid) 

ọdịdị Clear
njupụta 1.12g / cm 3 @ 25 ℃
viscosity 408cps @ 26 ℃
DP 0,18 mm
Ek 6.7 MJ / cm 2
Building oyi akwa ọkpụrụkpụ 0.1mm

 Mechanical Properties (Post-Cured)

n'ihe ule usoro URU Ọ BAARA
    90 nkeji UV post-na-agwọ
Ekweghị ekwe, Shore D ASTM D 2240 83
Flexural modulus, Mpa ASTM D 790 2,680-2,790
Flexural ike, Mpa ASTM D 790 75- 83
Tensile modulus, MPa ASTM D 638 2,580-2,670
Ike ọdụdọ, MPa ASTM D 638 45-60
Elongation na ezumike ASTM D 638 11-20%
Mmetụta ike, notched lzod, J / m  ASTM D 256  38 - 48 
Okpomọkụ nupụsịrị okpomọkụ, ℃  ASTM D 648 @ 66PSI  52 
Glass transition, Tg 

DMA, E' peak

62

 

 


  • Previous:
  • Next:

  •  

    Dị na otu Doppler ọsọ, mm / s Suggested single scanning speed, mm/s
    resin okpomọkụ 18-25℃ 23℃ without heating
    gburugburu ebe obibi iru mmiri 38% n'okpuru 36%below
    laser ike 300mw 300mw
    support scanning speed ≤1500 1200
    scanning interval ≤0.1mm 0.08mm
    Ngwe ịgụ isiokwu ọsọ
    ≤7000 2000
    Wet ịgụ isiokwu ọsọ ≥4000 7500

     

     