Resin SZUV-C6006-transparent

Short Description:

SZUV-C6006 is a transparent resin for SLA 3D printer.

3D Materials Printing


Detail prodottu

Video

Printing Instructions

Product Tags

3D Materials Printing

Transparent Resin-SZUV-C6006

Hierapolis di 3D Materials Printing

caratteristiche

SZUV-C6006

Description prodottu 

SZUV-C6006 is a clear SL resin which has accurate and durable features. It is designed for solid state SLA printers.

SZUV-C6006 can be applied in master patterns, concept models, general parts and functional prototypes in the field of automotive, medical and consumer electronics industries.

tipica CARATTERISTICHE

-Medium viscosity, so easy for recoating, easy to clean parts and machines 

-Improved strength retention, improved dimensions retention of parts in humid condition 

-Good strength, need minimal part finishing 

tipica benefici

-Superior clear, building parts with outstanding clarity and excellent accuracy 

-Need less part finishing time, easier post-curing 

Physical Properties (Liquid) 

aspettu U Populu Và
foltu 1.12g / CM 3 @ 25 ℃
Viscosity 408cps @ 26 ℃
Dp 0,18 mm in
E ec 6,7 MJ / cm Lingua 2
Building layer 0.1mm

 Mechanical Properties (Post-Cured)

misurazzioni TEST mètudu valore
    90-Minute UV post-rimediu
Temperature, riva D ASTM D 2240 83
canne Flexural, mpa ASTM D 790 2,680-2,790
forza Flexural, mpa ASTM D 790 75- 83
canne Tensile, mpa ASTM D 638 2,580-2,670
forza Tensile, mpa ASTM D 638 45-60
Longitudinalis a ruttura ASTM D 638 11-20%
forza Impact, emarginatus lzod, J / m  ASTM D 256  38 - 48 
Calori Temperature deflection, ℃  ASTM D 648 @ 66PSI  52 
Glass transition, Tg 

DMA, E' peak

62

 

 


  • Previous:
  • Next:

  •  

    Disponibile in sola scanning vitezza, MM / s Suggested single scanning speed, mm/s
    Temperature risina 18-25℃ 23℃ without heating
    umidità ambiente 38% sottu 36%below
    lu putiri lu laser 300mw 300mw
    support scanning speed ≤1500 1200
    scanning interval ≤0.1mm 0.08mm
    battutu circular enverrai
    ≤7000 2000
    Cumpleti battutu Scanning ≥4000 7500

     

     